As a new kind of 2D nanomaterials, graphene oxide(GO) with 2–4 layers was fabricated via a modi fied Hummers method and used for the preparation of pervaporation(PV) membranes. Such GO membranes were prepared via a facile vacuum-assisted method on anodic aluminium oxide disks and applied for the dehydration of butanol. To obtain GO membranes with high performance, effects of pre-treatments, including high-speed centrifugal treatment of GO dispersion and thermal treatment of GO membranes, were investigated. In addition, effects of operation conditions on the performance of GO membranes in the PV process and the stability of GO membranes were also studied. It is of bene fit to improve the selectivity of GO membrane by pre-treatment that centrifuges the GO dispersion with 10000 r·min-1for 40 min, which could purify the GO dispersion by removing the large size GO sheets. As prepared GO membrane showed high separation performance for the butanol/water system. The separation factor was 230, and the permeability was as high as 3.1 kg·m-2·h-1when the PV temperature was 50 °C and the water content in feed was 10%(by mass). Meanwhile, the membrane still showed good stability for the dehydration of butanol after running for 1800 min in the PV process. GO membranes are suitable candidates for butanol dehydration via PV process.