B/N掺杂富含{001}晶面锐钛矿TiO2的最佳可见光光电催化水氧化活性研究

查看详情 浏览次数:1
作者洪星星1,2 ; 康宇阳1,2 ; 甄超1 ; 康向东1 ; 尹利长1 ; John TS Irvine3 ; 王连洲4 ; 刘岗1,2 ; 成会明1 ; 5 ; 6
作者Xingxing Hong ; Yuyang Kang ; Chao Zhen ; Xiangdong Kang ; Li-Chang Yin ; John TS Irvine ; Lianzhou Wang ; Gang Liu ; Hui-Ming Cheng ; Shenyang National Laboratory for Materials Science ; Institute of Metal Research ; Chinese Academy of Sciences ; School of Materials Science and Engineering ; University of Science and Technology of China ; School of Chemistry ; University of St. Andrews ; Nanomaterials Centre ; School of Chemical Engineering and AIBN ; the University of Queensland ; Tsinghua-Berkeley Shenzhen Institute ; Tsinghua University ; Center of Excellence in Environmental Studies ; King Abdulaziz University
单位1Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences;2School of Materials Science and Engineering, University of Science and Technology of China;3School of Chemistry, University of St. Andrews;4Nanomaterials Centre, School of Chemical Engineering and AIBN, the University of Queensland;5Tsinghua-Berkeley Shenzhen Institute, Tsinghua University;6Center of Excellence in Environmental Studies, King Abdulaziz University收起
关键词锐钛矿TiO2 ; 可见光区 ; 氧化活性 ; 光电催化 ; N掺杂 ; 晶面 ; 热处理温度 ; 英文
来源Science China Materials
出版年2018
期号第6期
摘要
本文以锐钛矿TiO2微米球光催化材料为研究对象,其表面主要由{001}晶面组成,间隙掺杂硼原子在微米球中呈浓度梯度分布,浓度最高点位于表面.通过对其在氨气气氛、不同温度下(440–560℃)进行热处理,可实现氮替代晶格氧的掺杂,氮原子掺杂的浓度随着热处理温度的增加,由7.03增加到15.47 at%.随着掺杂氮浓度的增加,所得掺杂TiO2微米球的可见光吸收强度相应提高.进一步研究所得掺杂TiO2微米球的可见光光吸收、原子和电子结构与可见光光电催化水氧化活性的关联特性,发现在520℃下所得氮掺杂TiO2的可见光光电催化水氧化活性最大,该样品吸收光谱的显著特征是在可见光区吸光率高,且没有与缺陷相关联的背底吸收.